Optimising the bioactivity of alkaline-treated titanium alloy

M. Wei, H. M. Kim, T. Kokubo, J. H. Evans

Research output: Contribution to journalArticlepeer-review

124 Scopus citations

Abstract

A layer of sodium titanate hydrogel on titanium alloy (Ti6A14V) induces apatite formation in simulated body fluid (SBF). This paper seeks to determine the parameters of alkaline-treated and subsequent heat treatment which lead to the most rapid formation of apatite. Specimens were soaked in 3, 5, 10 or 15 M solutions of NaOH at temperatures of 60 or 80 °C for 1, 3 or 7 days. It was found that the optimum treatment for the Ti6A14V alloy was a 3-day soak in 5 M NaOH solution at 80 °C. Specimens treated under these optimum conditions were subsequently heat-treated at 500, 600, and 700 °C for 1 h so as to consolidate the sodium titanate hydrogel layer and improve its bonding to the substrate. Treatment at 600 °C resulted in the best bonding and the optimum rate of apatite formation. On soaking in simulated body fluid (SBF), apatite formed within 3 days, as compared to the 7-day formation, which was the best rate previously reported. The acceleration in the rate of apatite formation is significant, as it should allow for earlier load bearing of prostheses following implantation.

Original languageEnglish (US)
Pages (from-to)125-134
Number of pages10
JournalMaterials Science and Engineering C
Volume20
Issue number1-2
DOIs
StatePublished - May 31 2002
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • General Medicine

Fingerprint

Dive into the research topics of 'Optimising the bioactivity of alkaline-treated titanium alloy'. Together they form a unique fingerprint.

Cite this